Assessment of probable causes of corrosion damage of a mould made of cast iron
Sobola, Petr ; Pantělejev, Libor (referee) ; Man, Ondřej (advisor)
Bachelor’s thesis deals with solution of problems on glass moulds, which were exposed to the corrosion medium for up to two days causing their damage. The thesis contains theoretical analysis of the problem, layout for the corrosion experiment and its execution. Based on the experiment a conclusion was pronounced that the extent of damage which was observed was not able to be created by corrosion of initial surface without any previous defect.
Assessment of probable causes of corrosion damage of a mould made of cast iron
Sobola, Petr ; Pantělejev, Libor (referee) ; Man, Ondřej (advisor)
Bachelor’s thesis deals with solution of problems on glass moulds, which were exposed to the corrosion medium for up to two days causing their damage. The thesis contains theoretical analysis of the problem, layout for the corrosion experiment and its execution. Based on the experiment a conclusion was pronounced that the extent of damage which was observed was not able to be created by corrosion of initial surface without any previous defect.
Assessment of probable causes of corrosion damage of a mould made of cast iron
Sobola, Petr ; Pantělejev, Libor (referee) ; Man, Ondřej (advisor)
Bachelor’s thesis deals with solution of problems on glass moulds. Those moulds were exposed to the corrosion medium for up to two days which caused their damage. The thesis contains theoretical analysis of the problem, layout for the corrosion experiment and its execution. Based on the experiment a conclusion was pronounced that we cannot definitely say that 48 hours were enough to achieve as high the damage as was observed.